通风管道变形与哪些因素有关？

发布人：http://www.sftfgd.com   发布时间：2021-10-06 15:10:44

1、镁水泥在自然养护条件下其体积是一个连续膨胀过程，其线膨胀率为0.1-0.2%，体积膨胀率约为1%。

1. Under natural curing conditions, the volume of magnesium cement is a continuous expansion process, with linear expansion rate of 0.1-0.2% and volume expansion rate of about 1%.

2、菱镁矿在服烧过程中不可避免地产生局部过烧，使一部分MgO呈死烧状态，过烧的MgO水化过程很慢，当已形成强度的水泥石中的MgO再遇水进行水化时，生成Mg(OH)2，体积膨胀120%。

2. During the service burning process of magnesite, it is inevitable to produce local overburning, resulting in a part of MgO in a dead burning state. The hydration process of overburned MgO is very slow. When the MgO in the cement stone with formed strength is hydrated again with water, Mg (OH) 2 is generated, with a volume expansion of 120%.

3、轻烧氧化镁中游离CaO水化时体积膨胀90%，而卤片中存在着 SO42-，当Ca(OH)2转化成石膏时，固体体积将增加2倍以上，导致制品变形，这也是限制轻烧氧化镁中游离CaO含量、卤片中SO42-含量的原因。

3. The volume of free CaO in lightly burned magnesia expands by 90% during hydration, while there is SO42 - in halogen tablets. When Ca (OH) 2 is converted into gypsum, the solid volume will increase by more than twice, resulting in product deformation, which is also the reason for limiting the content of free CaO in lightly burned magnesia and the content of SO42 - in halogen tablets.

4、MgO-Mg-C12-H2O系统水化过程是一个强烈的放热反应过程，而生产的管道体积又大，若环境温度较高，则反应升温过程，板材本体温度过高，反应不充分，造成较大的结晶应力和热膨胀应力，使制品体积膨胀。

4. The hydration process of mgo-mg-c12-h2o system is a strong exothermic reaction process, and the volume of the produced pipeline is large. If the ambient temperature is high, the reaction temperature will rise. The plate body temperature is too high and the reaction is insufficient, resulting in large crystallization stress and thermal expansion stress, resulting in the volume expansion of the product.

以上的精彩内容来自：山东通风管道更多的精彩内容来自：http://www.sftfgd.com欢迎大家与我们进行交流。

The above highlights come from Shandong ventilation pipeline, and more highlights come from: http://www.sftfgd.com Welcome to communicate with us.